Optimizing phosphoric acid etching times across different formulations: Impact on dentin structure, roughness, and adhesive performance after 4 years
| dc.contributor.author | de Souza, Julian | |
| dc.contributor.author | Ñaupari-Villasante, Romina | |
| dc.contributor.author | Hass, Viviane | |
| dc.contributor.author | Arana Gordillo, Luis Alfonso | |
| dc.contributor.author | Gutiérrez, Mario Felipe | |
| dc.contributor.author | Gomes, Giovana Mongruel | |
| dc.contributor.author | Loguercio, Alessandro D. | |
| dc.contributor.author | Gomes, João Carlos | |
| dc.date.accessioned | 2025-07-18T19:36:09Z | |
| dc.date.available | 2025-07-18T19:36:09Z | |
| dc.date.issued | 2025-07 | |
| dc.description | Objetivo Evaluar el efecto de los tiempos de grabado con ácidos fosfóricos comerciales sobre el patrón de desmineralización, la rugosidad de la dentina, el mapeo químico, la nanofiltración (NL) y la resistencia de adhesión a la microtracción resina-dentina (μTBS) cuando se utiliza con un adhesivo de grabado y aclarado, evaluado inmediatamente y después de 4 años de almacenamiento en agua. Métodos Se probaron cuatro ácidos fosfóricos comerciales: Ultra-etch [ULE, 35 %], Scotchbond Universal Etchant [SUE, 32 %]; Dentsply Dental Conditioner [DDC, 37 %] y Total Etch [TTE, 37 %]. Se grabó la dentina oclusal de 188 molares durante 3 y 15 segundos. Se observaron patrones de desmineralización mediante SEM, se midió la rugosidad mediante perfilometría óptica y se obtuvo un mapa químico mediante espectroscopia micro-Raman. Se prepararon vigas unidas con resina-dentina para las pruebas NL y µTBS al inicio y después de 4 años de almacenamiento en agua. Los datos se evaluaron estadísticamente con ANOVA de tres vías y la prueba de Tukey (α = 0,05). Resultados Tras el grabado de 15 segundos, ULE mostró una desmineralización significativamente menor en comparación con DDC y TTE, mientras que SUE tuvo un efecto intermedio (p = 0,001). No se observaron diferencias entre los grupos tras el grabado de 3 segundos (p > 0,05). ULE y SUE mostraron una menor densidad tubular que DDC y TTE (p = 0,001). La rugosidad y el mapeo químico indicaron una menor desmineralización a los 3 segundos para todos los grupos (p < 0,002), excepto ULE, que mostró similar tanto a los 3 como a los 15 segundos (p > 0,05). Los valores de NL y μTBS fueron mayores para ULE y SUE, independientemente de los tiempos de grabado y el periodo de envejecimiento (p < 0,05). ULE demostró el mejor control sobre la desmineralización, seguido de SUE, mejorando ambos el rendimiento de adhesión resina-dentina. | |
| dc.description.abstract | Objective To evaluate the effect of etching times with commercial phosphoric acids on the demineralization pattern, dentin roughness, chemical mapping, nanoleakage (NL), and resin-dentin microtensile bond strength (μTBS) when used with an etch-and-rinse adhesive, assessed immediately and after 4 years of water storage. Methods Four commercial phosphoric acids were tested: Ultra-etch [ULE, 35 %], Scotchbond Universal Etchant [SUE, 32 %]; Dentsply Dental Conditioner [DDC, 37 %] and Total Etch [TTE, 37 %]. Occlusal dentin from 188 molars was etched for 3 and 15 seconds. Demineralization patterns were observed via SEM, roughness was measured using optical profilometry, and chemical mapping was obtained through micro-Raman spectroscopy. Resin-dentin bonded beams were prepared for NL and µTBS testing at baseline and after 4 years of water storage. Data were statistically evaluated with three-way ANOVA and Tukey’s test (α = 0.05). Results After 15-second etching, ULE exhibited significantly less demineralization compared to DDC and TTE, while SUE had an intermediate effect (p = 0.001). No differences were observed among groups after 3-second etching (p > 0.05). ULE and SUE showed lower tubular density than DDC and TTE (p = 0.001). Roughness and chemical mapping indicated lower demineralization at 3 seconds for all groups (p < 0.002), except ULE, which showed similar at both 3 and 15 seconds (p > 0.05). NL and μTBS values were higher for ULE and SUE, regardless of etching times and aging period (p < 0.05). ULE demonstrated the best control over demineralization, followed by SUE, both enhancing resin-dentin bonding performance. | |
| dc.identifier.citation | de Souza, J., Ñaupari-Villasante, R., Hass, V., Arana-Gordillo, L. A., Gutiérrez, M. F., Gomes, G. M., Loguercio, A. D., & Gomes, J. C. (2025). Optimizing phosphoric acid etching times across different formulations: Impact on dentin structure, roughness, and adhesive performance after 4 years. Dental Materials, 41(7), 850–861. https://doi.org/10.1016/j.dental.2025.05.004 | |
| dc.identifier.issn | 01095641 | |
| dc.identifier.uri | https://repositorio.usc.edu.co/handle/20.500.12421/7516 | |
| dc.language.iso | en | |
| dc.publisher | Elsevier Inc. | |
| dc.subject | Dental acid etching | |
| dc.subject | Dentin | |
| dc.subject | Longevity | |
| dc.subject | Tooth demineralization | |
| dc.title | Optimizing phosphoric acid etching times across different formulations: Impact on dentin structure, roughness, and adhesive performance after 4 years | |
| dc.type | Article |